Dear Professor Graeme Henkelman,
I'm trying to do a cNEB calculation of CO oxidation on In2O3. I use IOPT = 1, EDIFF = 1E-7, EDIFFG = -5E-02. The calculation didn't converge. I changed the paremeters to IOPT = 2 or 3, EDIFF = 1E-5, EDIFFG = -1E-01. Still it can't converge. I use images = 5. In another calculation In use mages = 10. I failed to converge,either. I attached my complete calculation files here. Could you please give me some comment about it?
Sincerely,
Hongbo
NEB Convergence problem
Moderator: moderators
NEB Convergence problem
- Attachments
-
- In2O3-110-Pd-O2-CO-2-neb.tgz
- (15.44 MiB) Downloaded 455 times
Re: NEB Convergence problem
This calculation look reasonable. The only issue I see is very high forces at the start of the calculation. Switch to a TIMESTEP of 0.01 and run about 20 iterations and make sure that the forces systematically drop from ~30 eV/Ang to <1 eV/Ang. Once all the forces are below 1 eV/Ang, you can go back to a TIMESTEP of 0.1. You could also use the IDPP method to set up your initial band with lower initial forces. This is easy to do and costs nothing; you can use the method within ASE or our nebmake.py script which will automatically use the IDPP method.
Re: NEB Convergence problem
Thank you Professor Graeme Henkelman. The problem solved by using a TIMESTEP of 0.01 first, and later using TIMESTEP of 0.05. But if I use a TIMESTEP of 0.01 first, and later I use TIMESTEP of 0.1, still it can't converged.
Re: NEB Convergence problem
Ok, it sounds like you have what you need to make things work. Great!